Polychloroprene Rubber
A sulfur-modified polychloroprene rubber with medium crystallization rate .Used in manufacture of rubber products such as cable shield, V-belt and synchronous belt. It is similar to Du Pont's neoprene type GNA and Denka'PM-40.
Description: A xanthogen-modified polychloroprene rubber with medium crystallization rate, good heat resistance and stability at elevated temperature. Used for manufacture of light-colored rubber products such as seals, dust cover, rubber covered roller, lining, hose coating. It is similar to DuPont's Neoprene type W and Denka's PM-40.
Executive Standard: Q/CHS 3-2005
Specification:
Item
|
Specification
|
CR1211
|
CR1212
|
CR-2321
|
CR-2322
|
Mooney viscosityHL 100 1+4
|
30-45
|
46-60
|
35-45
|
46-55
|
Mooney scorch MSt5, min
|
30
|
11
|
Tensile strength, MPa
|
24
|
12
|
500%/ Modulus at 500%, MPa
|
1~5
|
1~5
|
Elongation at break,%
|
900
|
750
|
Volatile matter,%
|
1.0
|
1.2
|
Ash content, %
|
1.0
|
1.2
|
Package: Package: woven polypropylene lined-kraft paper bags with a release poly ethylene liner, 25kg net wt.
Storage: Storage life: one year below 20ºCand half a year below 30ºC from the date of production.
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Packaging and transport: The product is massive plastic. It packed with high-pressure polyethylene film heat sealing then putted into wooden case for storage and transportation. Each block net weight is 25kg; each box net weight is 1050 kg. Pay attention to prevent exposure under sun or rain during transport process.
Storage: It should be stored in well-ventilated, clean and dry warehouses. Place under open-air and direct sunlight is forbidden.